Publikations Einzelansicht

Titel: Oligomerization of PbO-Vapor
 

Autor(en):
 
O. Knacke und A. von Richthofen
 
Journal: Zeitschrift für Physikalische Chemie
Jahr: 1994
Band: 187
Seite(n): 257-264


Zusammenfassung:
The oligomerization of PbO-vapor was determined by measuring partial pressures using Knudsen effusion mass spectrometry in the temperature range 838 to 1018 K. The vapor of yellow lead oxide consists mainly of PbO, (PbO)2, (PbO)4. The partial pressures Pi are lg (Pi/bar) = -14480/T + 7.847| -14734/T + 7.968| -13446/T + 7.090, respectively. The standard enthalpies and entropies at 25°C are as follows: h298/kJ mol-1 = 72.370| -137.137| -591.234, and s298/J K-1 mol-1 = 240.040| 319.122| 450.882. To differentiate between parent and fragment ions, the effusion mass spectrometry has been combined with an electrochemical Knudsen cell containing liquid lead of varying oxygen concentrations. — In addition, the electrochemical cell allows in situ precipitation of red or yellow oxide, PbOR or PbOY, in liquid lead. Emf measurements correspond to normal enthalpies of h0298/kJ mol-1 = -221.2 ± 1.2 and -218.7 ± 0.8 respectively.<br> Zusammenfassung <br>Die Oligomerisation von PbO-Dampf wurde massenspektrometrisch mit einer elektrochemischen Knudsen-Zelle im Temperaturbereich von 838—1018 K untersucht. Der Dampf über gelbem Bleioxid besteht hauptsächlich aus PbO, (PbO)2. (PbO)4, mit den Partialdrücken lg (Pi/bar) = -14480/T + 7,847| -14734/T + 7,968| -13446/T + 7,090. Die Standardenthalpien und -entropien sind h298/kJ mol-1 = 72,370| -137,137| -591,234; s298/J K-1 mol-1 = 240,040| 319,122| 450,882. Zur Unterscheidung von Parent- und Fragmentionen wurde flüssiges Blei mit unterschiedlichen Sauerstoffkonzentrationen verwendet, die elektrochemisch gemessen wurden. —Die elektrochemische Knudsenzelle erlaubt auch eine reproduzierbare Fällung von rotem oder gelbem Bleioxid, PbOR oder PbOY, aus flüssigem Blei. EMK-Messungen ergaben die Normalenthalpien h0298/kJ mol-1 = -221,2 ± 1,2 und -218,7 ± 0,8.

Zurück zur Listen Ansicht

Publikations Einzelansicht

Titel: Oligomerization of PbO-Vapor
 

Autor(en):
 
O. Knacke und A. von Richthofen
 
Journal: Zeitschrift für Physikalische Chemie
Jahr: 1994
Band: 187
Seite(n): 257-264


Zusammenfassung:
The oligomerization of PbO-vapor was determined by measuring partial pressures using Knudsen effusion mass spectrometry in the temperature range 838 to 1018 K. The vapor of yellow lead oxide consists mainly of PbO, (PbO)2, (PbO)4. The partial pressures Pi are lg (Pi/bar) = -14480/T + 7.847| -14734/T + 7.968| -13446/T + 7.090, respectively. The standard enthalpies and entropies at 25°C are as follows: h298/kJ mol-1 = 72.370| -137.137| -591.234, and s298/J K-1 mol-1 = 240.040| 319.122| 450.882. To differentiate between parent and fragment ions, the effusion mass spectrometry has been combined with an electrochemical Knudsen cell containing liquid lead of varying oxygen concentrations. — In addition, the electrochemical cell allows in situ precipitation of red or yellow oxide, PbOR or PbOY, in liquid lead. Emf measurements correspond to normal enthalpies of h0298/kJ mol-1 = -221.2 ± 1.2 and -218.7 ± 0.8 respectively.<br> Zusammenfassung <br>Die Oligomerisation von PbO-Dampf wurde massenspektrometrisch mit einer elektrochemischen Knudsen-Zelle im Temperaturbereich von 838—1018 K untersucht. Der Dampf über gelbem Bleioxid besteht hauptsächlich aus PbO, (PbO)2. (PbO)4, mit den Partialdrücken lg (Pi/bar) = -14480/T + 7,847| -14734/T + 7,968| -13446/T + 7,090. Die Standardenthalpien und -entropien sind h298/kJ mol-1 = 72,370| -137,137| -591,234; s298/J K-1 mol-1 = 240,040| 319,122| 450,882. Zur Unterscheidung von Parent- und Fragmentionen wurde flüssiges Blei mit unterschiedlichen Sauerstoffkonzentrationen verwendet, die elektrochemisch gemessen wurden. —Die elektrochemische Knudsenzelle erlaubt auch eine reproduzierbare Fällung von rotem oder gelbem Bleioxid, PbOR oder PbOY, aus flüssigem Blei. EMK-Messungen ergaben die Normalenthalpien h0298/kJ mol-1 = -221,2 ± 1,2 und -218,7 ± 0,8.

Zurück zur Listen Ansicht